MULTILAYER CERAMIC CHIP CAPACITORS
Capacitance & Tolerance
1R0 = 1.0pF 100 = 10pF 101 = 100pF 102 = 1000pF = 1nF 103 = 10000pF = 10nF 104 = 100nF 105 = 1000nF = 1uF 106 = 10000nF = 10uF B = 0.1pF (Cap 5pF) C = 0.25pF (Cap 5pF) D = 0.5pF (5pF Cap 10pF) J = 5% K = 10% M = 20% Z = -20%+80%
NPO
X7R
Y5V
1RO ~ 103
101 ~ 105
103 ~ 106
B, C, D, J, K
J, K, M
M, Z
PILKOR ELECTRONICS CO., LTD.
Dielectric
NPO
EIA Cap Size 1005(0402) 1608(0603) 2012(0805) 3216(1206) 3225(1210) 4532(1812) Code VDCW 10V 16V 25V 50V 10V 16V 25V 50V 10V 16V 25V 50V 10V 16V 25V 50V 10V 16V 25V 50V 10V 16V 25V 50V 0R5 0.5pF 1R0 1 1R2 1.2 1R5 1.5 1R8 1.8 2R2 2.2 2R7 2.7 3R3 3.3 3R9 3.9 4R7 4.7 5R6 5.6 6R8 6.8 8R2 8.2 100 10pF 120 12 150 15 180 18 220 22 270 27 330 33 390 39 470 47 560 56 680 68 820 82 101 100pF 121 120 151 150 181 180 221 220 271 270 331 330 391 390 471 470 561 560 681 680 821 820 102 1000pF 122 1200 152 1500 182 1800 222 2200 272 2700 332 3300 392 3900 472 4700 562 5600 682 6800 822 8200 103 0.01uF
N
S
A
B
C
B
D
D
Other size and capacitance and voltage and 13 reel are available upon customer's request.
Tape and Reel -
-
MULTILAYER CERAMIC CHIP CAPACITORS
Dielectric EIA Cap Code 0R5 1R0 1R2 1R5 1R8 2R2 2R7 3R3 3R9 4R7 5R6 6R8 8R2 100 120 150 180 220 270 330 390 470 560 680 820 101 121 151 181 221 271 331 391 471 561 681 821 102 122 152 182 222 272 332 392 472 562 682 822 103 123 153 183 223
NPO
3225(1210) 4532(1812) 4520(1808) Size 1608(0603) 2012(0805) 3216(1206) VDCW 100 100 200 250 500 100 200 250 500 1000 2000 100 200 250 500 1000 2000 100 200 250 500 1000 2000 1000 2000 3000 0.5pF 1 1.2 1.5 1.8 2.2 2.7 3.3 3.9 4.7 5.6 6.8 8.2 10pF 12 15 18 22 27 33 39 47 56 68 82 100pF 120 150 180 220 270 330 390 470 560 680 820 1000pF 1200 1500 1800 2200 2700 3300 3900 4700 5600 6800 8200 0.01uF 0.012 0.015 0.018 0.022
A
B
C
C
D
K
Other size and capacitance and voltage and 13 reel are available upon customer's request.
Tape and Reel -
-
PILKOR ELECTRONICS CO., LTD.
Dielectric EIA Cap Size Code VDCW 101 100pF 121 120 151 150 181 180 221 220 271 270 331 330 391 390 471 470 561 560 681 680 821 820 102 1000pF 122 1200 152 1500 182 1800 222 2200 272 2700 332 3300 392 3900 472 4700 562 5600 682 6800 822 8200 103 0.01uF 123 0.012 153 0.015 183 0.018 223 0.022 273 0.027 333 0.033 393 0.039 473 0.047 563 0.056 683 0.068 823 0.082 104 0.1uF 154 0.15 184 0.18 224 0.22 334 0.33 474 0.47 564 0.56 824 0.82 105 1uF
X7R 1005(0402) 1608(0603) 2012(0805) 3216(1206) 3225(1210) 4532(1812) 10V 16V 25V 50V 10V 16V 25V 50V 10V 16V 25V 50V 10V 16V 25V 50V 10V 16V 25V 50V 10V 16V 25V 50V
N S B C D
D D
Other size and capacitance and voltage and 13 reel are available upon customer's request.
Tape and Reel -
-
-
MULTILAYER CERAMIC CHIP CAPACITORS
Dielectric EIA Cap Code 101 121 151 181 221 271 331 391 471 561 681 821 102 122 152 182 222 272 332 392 472 562 682 822 103 123 153 183 223 273 333 393 473 563 683 823 104 124 154 184 224 334 474 684 824 105
X7R
3225(1210) 4532(1812) 4520(1808) 2012(0805) 3216(1206) Size 1608(0603) VDCW 100 100 200 250 500 100 200 250 500 1000 1500 2000 100 200 250 500 1000 100 200 250 500 1000 2000 1000 1500 2000 100pF 120 150 180 220 270 330 390 470 560 680 820 1000pF K 1200 1500 1800 2200 D 2700 3300 3900 4700 5600 6800 8200 0.01uF 0.012 0.015 0.018 0.022 0.027 0.033 0.039 0.047 0.056 D 0.068 K 0.082 0.1uF 0.12 0.15 0.18 K 0.22 0.33 0.47 0.68 K 0.82 1uF
B
G
C
C
D
Other size and capacitance and voltage and 13 reel are available upon customer's request.
PILKOR ELECTRONICS CO., LTD.
Dielectric
Y5V
EIA Cap Size 1005(0402) 1608(0603) 2012(0805) 3216(1206) 3225(1210) 4532(1812) Code VDCW 10V 16V 25V 50V 10V 16V 25V 50V 10V 16V 25V 50V 10V 16V 25V 50V 10V 16V 25V 50V 10V 16V 25V 50V 102 1000pF 122 1200 152 1500 182 1800 222 2200 272 2700 332 3300 392 3900 472 4700 562 5600 682 6800 822 8200 103 0.01uF 123 0.012 153 0.015 183 0.018 223 0.022 273 0.027 333 0.033 393 0.039 473 0.047 563 0.056 683 0.068 823 0.082 104 0.1uF 154 0.15 224 0.22 334 0.33 474 0.47 684 0.68 D 105 1.0uF 155 1.5 D 225 2.2 335 3.3 475 4.7 D G 106 10uF
N
S
A
B
C
C
D
Other size and capacitance and voltage and 13 reel are available upon customer's request. Tape and Reel
MULTILAYER CERAMIC CHIP CAPACITORS
Dielectric EIA Cap Code 103 123 153 183 223 273 333 393 473 563 683 823 104 154 224 334 684 105 Size VDCW 0.01uF 0.012 0.015 0.018 0.022 0.027 0.033 0.039 0.047 0.056 0.068 0.082 0.1uF 0.15 0.22 0.33 0.68 1.0 100 2012(0805) 200 250
Y5V 100 3216(1206) 200 250 100 3225(1210) 200 250
B C D
Other size and capacitance and voltage and 13 reel are available upon customer's request.
PILKOR ELECTRONICS CO., LTD.
No 1
Test Items Visual & Mechanical
Test Conditions
Requirements No remarkable defect. Dimensions to conform to individual specification sheet.
2
Capacitance
1000pF 1000pF
1.0 0.2Vrms, 1MHz 10% 1.0 0.2Vrms, 1KHz 10% 1.0 0.2Vrms, 1MHz 10% 1.0 0.2Vrms, 1KHz 10%
Shall not exceed the limits given in the detailed spec.
3
Q Value
1000pF 1000pF
More than 30pF : Q 1000 Less than 30pF : Q 400+20C
4
Dielectric strength
Rated Voltage : 50V To apply voltage : 250% of rated voltage for 1~5 sec. Charge & discharge current less than 50mA. Rated Voltage : 100V 200V~300V 500V~999V 1000V~3000V Cut-off, set at 10mA TEST=15 RAMP=0
No evidence of damage or flash over during test.
100V 200V~300V 500V~999V 1000V~3000V 10G 10G 10G
=3 times VDC =2 times VDC =1.5 times VDC =1.2 times VDC
5
Insulation resistance
Rated Voltage : 50V To apply rated voltage for max. 120sec. Rated Voltage : 100V~500V Rated Voltage : 500V To apply rated Voltage To apply 500V 60sec at 25
MIN. or 500 -F MIN., whichever is smaller.
6 7
Temperature coefficient Bending test
With no electrical load -55~125
Within
30ppm/
The middle part of substrate shall be pressurized by means of the pressurizing rod at a rate of about 1mm per second until the deflection becomes 1mm and then the pressure shall be maintained for 5sec.(Appendix 1) Mesurement to be made after keeping at room temp. for 24 2 hours. Solder temperature : 230 5 Dipping time : 2 0.5sec Solder : SN63A Solder temperature : 260 5 Dipping time : 10 1sec Solder : SN63A Mesurement to be made after keeping at room temp. for 24 2 hours.
No remarkable damage. Cap change : 5.0%MAX. or 0.5pF MAX., whichever is larger. This capacitance change means the change of capacitance under specified flexure of substrate from the capacitance mesured before the test. 90%MIN. coverage of all metallized area.
8
Solderability
9
Resistance to soldering heat
No remarkable damage. Cap change : 2.5%MAX. or 0.25pF MAX., whichever is large. Q & I.R. & Dielectric strength : To meet initial requirements. 25%max. Leaching on each edge.
MULTILAYER CERAMIC CHIP CAPACITORS
No 10
Test Items Temperature cycle
Test Conditions Test temp : -55~125 Test step : 1)-55 -3/+0 30 3min. 2)room temp. 2~3min. 3)125 +3/-0 30 2min. 4)room temp. 2~3min. Conduct the five cycles according to the temperatures and time. Measurement to be made after keeping at room temp. for 24 2 hours. Test temp : 40 2 Humidity : 90~95%RH Test time : 1000+24/-0 hours. Measurement to be made after keeping at room temp. for 24 2 hours.
Requirements No remarkable damage. Cap change : 2.5%MAX. or 0.25pF MAX., whichever is larger. Q & I.R. & Dielectric strength : To meet initial requirements.
11
Humidity(Damp Heat) steady state
No remarkable damage. Cap change : 5.0%MAX. or 0.5pF MAX., whichever is larger. Q value : More than 30pF Q 350 10pF C 30pF Q 275+2.5C Less than 10pF Q 200+10C I.R. : 1G MIN. or 50 -F MIN., whichever is smaller. No remarkable damage. Cap change : 7.5%MAX. or 0.75pF MAX., whichever is larger. Q value : More than 30pF Q 200 C 30pF Q 100+10/3C I.R. : 500M MIN. or 25 -F MIN., whichever is smaller. No remarkable damage or removal of the terminations. No remarkable damage. Cap change & Q : To meet initial requirements.
12
Humidity(Damp Heat) Load
Test temp : 40 2 Humidity : 90~95%RH Test time : 1000+24/-0 hours. To apply voltage : rated voltage. Measurement to be made after keeping at room temp. for 24 2 hours. Pressurizing force : 1kg(10N) Test time : 10 1sec(Appendix 2) Vibration frequency : 10~55Hz/min. Total amplitude : 1.5mm Test time : 6 hours. (Two hours each in three mutually perpendicular directions.) Test temp : 125 3 To apply voltage : 200% of rated voltage Test time : 1000+24/-0 hours. Measurement to be made after keeping at room temp. for 24 2 hours.
13 14
Adhesive strength of termination Vibration Resistance
15
High Temperature Load (Endurance)
No remarkable damage. Cap change : 3.0%MAX. or 0.3pF MAX., whichever is larger. Q value : More than 30pF Q 350 10pF C<30pF Q 275+2.5C Less than 10pF Q 200+10C I.R. : 1G MIN. or 50 -F MIN., whichever is smaller.
High voltage products' reliability items depend on customer's request.
PILKOR ELECTRONICS CO., LTD.
No 1
Test Items Visual & Mechanical
Test Conditions
Requirements No remarkable defect. Dimensions to conform to individual specification sheet.
2 3
Capacitance Dissipation factor
1.0 0.2Vrms, 1KHz 10% 1.0 0.2Vrms, 1KHz 10%
Shall not exceed the limits given in the detailed spec. 2.5% Rated voltage : 50V 3.5% Rated voltage : 25V, 16V 5.0% Rated voltage : 10V No evidence of damage or flash over during test.
4
Dielectric strength
Rated Voltage : 50V To apply voltage : 250% of rated voltage for 1~5 sec. Charge & discharge current less than 50mA. Rated Voltage : 100V 200V~300V 500V~999V 1000V~3000V Cut-off, set at 10mA TEST=15 RAMP=0
100V 200V~300V 500V~999V 1000V~3000V 10G 10G 10G
=3 times VDC =2 times VDC =1.5 times VDC =1.2 times VDC
5
Insulation resistance
Rated Voltage : 50V To apply rated voltage for max. 120sec. Rated Voltage : 100V~500V Rated Voltage : 500V To apply rated Voltage To apply 500V 60sec at 25
MIN. or 500 -F MIN., whichever is smaller.
6 7
Temperature coefficient Bending test
With no electrical load -55~125
Within
15%
The middle part of substrate shall be pressurized by means of the pressurizing rod at a rate of about 1mm per second until the deflection becomes 1mm and then the pressure shall be maintained for 5sec.(Appendix 1) Mesurement to be made after keeping at room temp. for 24 2 hours. Solder temperature : 230 5 Dipping time : 2 0.5sec Solder : SN63A Solder temperature : 260 5 Dipping time : 10 1sec Solder : SN63A Mesurement to be made after keeping at room temp. for 48 4 hours.
No remarkable damage. 12.5% Cap change : This capacitance change means the change of capacitance under specified flexure of substrate from the capacitance mesured before the test.
8
Solderability
90%MIN. coverage of all metallized area.
9
Resistance to soldering heat
No remarkable damage. Cap change : 7.5% DF value & I.R. : To meet initial standard value. Dielectric strength : no defect.
MULTILAYER CERAMIC CHIP CAPACITORS
No 10
Test Items Temperature cycle
Test Conditions Test temp : -55~125 Test step : 1)-55 -3/+0 30 3min. 2)room temp. 2~3min. 3)125 +3/-0 30 2min. 4)room temp. 2~3min. Conduct the five cycles according to the temperatures and time. Measurement to be made after keeping at room temp. for 48 4 hours. Test temp : 40 2 Humidity : 90~95%RH Test time : 1000+24/-0 hours. Measurement to be made after keeping at room temp. for 48 4hours.
Requirements No remarkable damage. Cap change : 7.5% DF value & I.R. : To meet initial standard value.
11
Humidity(Damp Heat) steady state
No remarkable damage. Cap change : 12.5% DF value : 3.0% Rated voltage : 50V 5.0% Rated voltage : 25V, 16V 7.5% Rated voltage : 10V I.R. : 1G MIN. or 50 -F MIN., whichever is smaller. No remarkable damage. Cap change : 12.5% DF value : 3.0% Rated voltage : 50V 5.0% Rated voltage : 25V, 16V 7.5% Rated voltage : 10V I.R. : 500M MIN. or 25 -F MIN., whichever is smaller. No remarkable damage or removal of the terminations. No remarkable damage. Cap change & DF : To meet initial requirements.
12
Humidity(Damp Heat) Load
Test temp : 40 2 Humidity : 90~95%RH Test time : 1000+24/-0 hours. To apply voltage : rated voltage Measurement to be made after keeping at room temp. for 48 4 hours. Pressurizing force : 1kg(10N) Test time : 10 1sec(Appendix 2) Vibration frequency : 10~55Hz/min. Total amplitude : 1.5mm Test time : 6 hours. (Two hours each in three mutually perpendicular directions.) Test temp : 125 3 To apply voltage : 200% of rated voltage Test time : 1000+24/-0 hours. Measurement to be made after keeping at room temp. for 48 4 hours.
13 14
Adhesive strength of termination Vibration Resistance
15
High Temperature Load (Endurance)
No remarkable damage. Cap change : 12.5% DF value : 3.0% Rated voltage : 50V 5.0% Rated voltage : 25V, 16V 7.5% Rated voltage : 10V I.R. : 1G MIN. or 50 -F MIN., whichever is smaller.
High voltage products' reliability items depend on customer's request.
PILKOR ELECTRONICS CO., LTD.
No 1
Test Items Visual & Mechanical
Test Conditions
Requirements No remarkable defect. Dimensions to conform to individual specification sheet.
2 3
Capacitance Dissipation factor
1.0 0.2Vrms, 1KHz 10%, 25 1.0 0.2Vrms, 1KHz 10%, 25
Shall not exceed the limits given in the detailed spec. DF 5.0%(50V ) DF 5.0%(25V) Except 0603 0.1 ; 0805 0.33 1206 1 , DF 7% DF 7.0%(C 1.0 , 16V) ; DF 9.0%(C 1.0 , 16V) ; DF 12.5%(10V) No evidence of damage or flash over during test.
4
Dielectric strength
Rated Voltage : 50V To apply voltage : 250% of rated voltage for 1~5 sec. Charge & discharge current less than 50mA. Rated Voltage : 100V 200V~300V 500V~999V 1000V~3000V Cut-off, set at 10mA TEST=15 RAMP=0
100V 200V~300V 500V~999V 1000V~3000V 10G 10G 10G
=3 times VDC =2 times VDC =1.5 times VDC =1.2 times VDC
5
Insulation resistance
Rated Voltage : 50V To apply rated voltage for max. 120sec. Rated Voltage : 100V~500V Rated Voltage : 500V To apply rated Voltage To apply 500V 60sec at 20
MIN. or 500 -F MIN., whichever is smaller.
6 7
Temperature coefficient Bending test
With no electrical load -25~85
Within +30% / -80% No remarkable damage. 30% Cap change : This capacitance change means the change of capacitance under specified flexure of substrate from the capacitance mesured before the test.
The middle part of substrate shall be pressurized by means of the pressurizing rod at a rate of about 1mm per second until the deflection becomes 1mm and then the pressure shall be maintained for 5sec.(Appendix 1) Mesurement to be made after keeping at room temp. for 48 4 hours. Solder temperature : 230 5 Dipping time : 2 0.5sec Solder : SN63A Solder temperature : 260 5 Dipping time : 10 1sec Solder : SN63A Mesurement to be made after keeping at room temp. for 48 4 hours.
8
Solderability
90%MIN. coverage of all metallized area.
9
Resistance to soldering heat
No remarkable damage. Cap change : 20% DF value & I.R. : To meet initial standard value. Dielectric strength : no defect. 25% max. Leaching on each edge.
MULTILAYER CERAMIC CHIP CAPACITORS
No 10
Test Items Temperature cycle
Test Conditions Test temp : -25~85 Test step : 1)-25 -3/+0 2)room temp. 30 3min. 2~3min.
Requirements No remarkable damage. Cap change : 20% DF value & I.R. : To meet initial standard value. 3)85 +3/-0 30 2min.
4)room temp. 2~3min. Conduct the five cycles according to the temperatures and time. Measurement to be made after keeping at room temp. for 48 4 hours. 11 Humidity(Damp Heat) steady state Test temp : 40 2 Humidity : 90~95%RH Test time : 1000+24/-0 hours. Measurement to be made after keeping at room temp. for 48 4hours. No remarkable damage. Cap change : 30% DF value : 7.5% Rated voltage : 50V 7.5% Rated voltage : 25V Except 0603 0.1 ; 0805 0.33 1206 1 , DF 10% DF 10.0%(C 1.0 , 16V) ; DF 12.5%(C 1.0 , 16V) ; DF 15%(10V) I.R. : 1G MIN. or 50 -F MIN., whichever is smaller. No remarkable damage. Cap change : 30% DF value : 7.5% Rated voltage : 50V 7.5% Rated voltage : 25V Except 0603 0.1 ; 0805 0.33 1206 1 , DF 10% DF 10.0%(C 1.0 , 16V) ; DF 12.5%(C 1.0 , 16V) ; DF 15%(10V) I.R. : 25 -F MIN. or 500M -F MIN., whichever is smaller. No remarkable damage or removal of the terminations. No remarkable damage. Cap change & DF : To meet initial requirements.
12
Humidity(Damp Heat) Load
Test temp : 40 2 Humidity : 90~95%RH Test time : 1000+24/-0 hours. To apply voltage : rated voltage Measurement to be made after keeping at room temp. for 48 4 hours.
13 14
Adhesive strength of termination Vibration Resistance
Pressurizing force : 1kg(10N) Test time : 10 1sec(Appendix 2) Vibration frequency : 10~55Hz/min. Total amplitude : 1.5mm Test time : 6 hours. (Two hours each in three mutually perpendicular directions.) Test temp : 85 3 To apply voltage : 200% of rated voltage Test time : 1000+24/-0 hours. Measurement to be made after keeping at room temp. for 48 4 hours.
15
High Temperature Load (Endurance)
No remarkable damage. Cap change : 30% DF value : 7.5% Rated voltage : 50V 7.5% Rated voltage : 25V Except 0603 0.1 ; 0805 0.33 1206 1 , DF 10% DF 10.0%(C 1.0 , 16V) ; DF 12.5%(C 1.0 , 16V) ; DF 15%(10V) I.R. : 1G MIN. or 50 -F MIN., whichever is smaller.
High voltage products' reliability items depend on customer's request.
PILKOR ELECTRONICS CO., LTD.
Size 1005(0402) 1608(0603) 2012(0805)
T (mm) (0.60 ~ 0.40) (0.90 ~ 0.70) (0.70 ~ 0.50) (0.90 ~ 0.70) (1.05 ~ 0.85) (1.35 ~ 1.05) (0.90 ~ 0.70) (1.05 ~ 0.85) (1.35 ~ 1.05) (1.05 ~ 0.85) (1.35 ~ 1.05) (1.35 ~ 1.05)
Tape Paper tape Paper tape Paper tape Paper tape Plastic tape Plastic tape Paper tape Plastic tape Plastic tape Plastic tape Plastic tape Plastic tape
Quantity 10Kpcs/reel 4Kpcs/reel 4Kpcs/reel 4Kpcs/reel 3Kpcs/reel 3Kpcs/reel 4Kpcs/reel 3Kpcs/reel 3Kpcs/reel 3Kpcs/reel 3Kpcs/reel 1Kpcs/reel
3216(1206)
3225(1210) 4532(1812)

▲Up To Search▲

Price & Availability of 0805B104XXX

	To Download 0805B104XXX Datasheet File
If you can't view the Datasheet, Please click here to try to view without PDF Reader .