type 3613c series product ? specification 1 st april 2003 issue 5 telephone tyco passive product support team ++ 44 (0) 1793 572484 website ? www.resistors.t ycoelectronics.com email ? passivesales@t ycoelectronics.com page 1 of 4 moulded chip inductor 18:12 type 3613c series specially developed for automatic mounting applications, this exciting range of chip inductors are ferrite based and sealed in a thermoset plastic body. they employ solder coated copper terminations with barrier layer. customers can therefore expect consistent quality, performance and reliability. its smooth top surface makes it particularly well suited to pick and place equipments. truly the last word in 1812 chip inductors. key features ? high reliability ? two versatile types ? small versatile size - 3.2 x 4.5 mm ? temperature range -25 c to +100 c ? supplied in standard carrier tape ? suitable for dip and wave solder ? insulation 1000m r min ? available from stock stockists: this product is available from farnell.
type 3613c series product ? specification 1 st april 2003 issue 5 telephone tyco passive product support team ++ 44 (0) 1793 572484 website ? www.resistors.t ycoelectronics.com email ? passivesales@t ycoelectronics.com page 2 of 4 3613c style operating characteristics 5% tolerance available on selected value ranges. please enquire.
type 3613c series product ? specification 1 st april 2003 issue 5 telephone tyco passive product support team ++ 44 (0) 1793 572484 website ? www.resistors.t ycoelectronics.com email ? passivesales@t ycoelectronics.com page 3 of 4 dimensions packaging (reel) packaging (tape) environmental test notes insulation: 1000 m ohms the measuring method for th e test data given overpage are as follows: temperature range: -25c to +85c ? l/l within 10% inductance: direct reading from q- meter (equivalent to yhp 4342a, jig used) q: direct reading from q-meter (equivalent to yhp 4342a, jig used) humidity load life: ? l/l within 5% self resonant frequency: grid dipo me ter (equivalent to measurement m159) dc resistance: wheatstone bridge (equivalent to yew 2755) vibration (see test method): unless otherwise specified, the temperature is 20c 5c and the humidity is 65% 20% how to order
type 3613c series product ? specification 1 st april 2003 issue 5 telephone tyco passive product support team ++ 44 (0) 1793 572484 website ? www.resistors.t ycoelectronics.com email ? passivesales@t ycoelectronics.com page 4 of 4 test methods item standard test method dc superposition characteristics ? l/l within -10% when the allowable current was applied, the inductance was measured with a yhp 4262a a nd compared with the initial value. temperature rise within 20c when the allowable current was applied, the amount of temperature rise was measured by the change in resistance. temperature rise ? l/l within 5% measurements were taken in a temperature range of -25c to 85c and the value at +20c was used as the standard value. overcurrent test no smoke and no fire twice the allowable current was applied for a period of five minutes. soldering heat resistance test no pronounced abnormality in appearance immersion twice for a period of 5 0.5 seconds in h63a solder at a temperature 260c 5c solderability not less than 90% bonding to electrode surfaces immersion for a period of 2 0.5 seconds in h63a solder at a temperature of 230 5c. flux used was a rosin-core solution containing approximately 25% methanol. insulation resistance not less than 1000 m 0.3mm diameter copper wires were wound around the coils three times and measurements were taken after 250vdc was applied between the wire and the terminals for a period of 1 minute. tensile strength test no separation from substrate after the inductors were solder ed to substrates, a force of 1.0kg was applied in both the x and y directions for a period of 5 seconds. stress test no breakage after the inductors were mounted on substrates, 1-mins. 10- 55-10 cycle per seconds sweeps 1.5mm stroke vibrations were applied for 2 hrs. each in the x, y and z directions drop test no pronounced abnormality in appearance the inductors were dropped 10 times from a height of 1.0 metre onto a concrete floor. vibration test ? l/l within 10% q not less than 30 after the inductors were mounted on substrates, 1-mins. 10- 55-10 cycle per seconds sweeps 1.5mm stroke vibrations were applied for 2 hours each in the x, y and z directions humidity resistance load test ? l/l within 10% q not less than 30 measurements were taken after the allowable current was applied while the inductors were stored at 60c 2c in 90 to 95% rh for a period of 500 hours. low temperature resistance test ? l/l within 10% q not less than 30 measurements were taken after the inductors were stored at - 40c 2c for period 1000 hours temperature cycle test ? l/l within 10% q not less than 30 measurements were taken after the inductors were stored for 30 minutes, during which they were subjected to 20 temperature cycles of between -25c and +85c. high temperature resistance load test ? l/l within 10% q not less than 30 measurements were taken after the allowable was applied while the inductors were stored at 85c for a period of 1000 hours. this publication is issued to provide outline information only and (unless specifically agreed to the contrary by the company i n writing) is not to form part of any order or be regarded as a representation relating to th e products or service concerned. we reserv e the right to alter without notice the sp ecification, design, pric e or conditions of supply of any product or service. whilst ty co electronics components products are of the very highest quality and reliability, all electronic compone nts can occasionally be subject to failure. where failure of a tyco electronics components product coul d result in life threat ening consequences, then the circuit and application must be discussed with the company. such areas might include ecg, respiratory and other medical and nuclear applica tions and any no n fail-safe applications circuit.
|